CP 370
Direct to metal converter of acrylic mixing systems
DTM is used in combination with Profix acrylic mixing systems to create a product that can be applied directly. to non-primed metal surfaces. The combination of the ACRYL / LV CRYL system with CP 370 DTM creates a corrosion-resistant coating. Such mixture can be applied in one or two coats to suitably prepared substrates. Key properties include excellent adhesion and corrosion protection on all metal substrates such as steel, aluminium and galvanised steel. Its high mechanical resistance makes the topcoat a perfect selection for cost-effective industrial applications.
- Product benefits: Smooth surface Easy application High paint efficiency Uniform surface Various degrees of satin effect
- Spill: 1.00 l / 3.50 l
Specification
Industry use
VARIOUS DEGREES OF
SATIN EFFECT
HIGH RESISTANCE
SMOOTH SURFACE
UNIFORM SURFACE
EASY
APPLICATION
125-190 μm
~7-9 m2/L
1.5 hrs
1 coat ~30 μm
CP 370: 24 months in originally
sealed packaging
CP 282/ CP 285/ CP 286:
12 months in originally sealed
packaging
Application
The surface is degreased with CP 015. The primer is then applied to the surface sanded with P320-P400 abrasives. Can be applied directly to bare metal surfaces
Preparation of ACRYL with CP 370 Semi-satin surface 70 parts parts of ACRYL 30 parts parts of CP 370 Satin surface 50 parts parts of ACRYL 50 parts parts of CP 370 Ready-to-spray mixture 100 parts parts of ACRYL+CP 370 mixture 25 parts parts of hardener CP 285 Alternative hardeners CP 282 (fast) < 15°C CP 286 (slow) > 25°C 15-25 parts by vol. of thinner CP 040/ 070/ 075
Nozzle size: 1.4-1.6 mm; Operating pressure: HVLP/RP 1.8-2.0 bar
2 full coats allowing flash-off between coats
5-10 min after coating at 20°C and 65% relative humidity
Drying times at 20°C and 65% relative humidity: - dust dryness: 10 min - for assembly: 5 hrs - thoroughly: 10 hrs Drying times at 60°C and 65% relative humidity: - for assembly: 30 min